Product description: Resin for 3D Printer FormFutura Platinum SLA Series 0,5 kg - Solid Granite Black
Solidblackphotopolymer resin. Used in open source3D printers, compatible with SLA, DLP and LCD technologies. Theresinis cured by a light wave of the length ranging from385 nm to 405 nm. It gives off a slightly unpleasant but non-intrusive odour when the print is formed. The finished models have a high level of detail and a smooth surface. Package contains0.5 kg of the product.
FormFutura Platinum SLA Series Resin.
Models made of FormFutura Platinum SLA Series resin.
Main features of the Platinum SLA Series resin
- Enable high resolution 3D printing. Provide very high detail of the model.
- Emitted during the printing unpleasant smell is not intense.
- Platinum SLA resins have high dimensional accuracy and low shrinkage
- They show low water absorption
- Platinum SLA Series resins are compatible with open source 3D printers that use light in the wavelength range of 385 nm to 405 nm to cure the print material.
- Main applications of Platinum SLA Series resins: figure printing, functional prototyping
Steps to be taken before printing
- Before each use, shake the bottle for at least 2 minutes.
- Then leave the resin for about 10 minutes to let the air bubbles escape from the resin
- After printing, unused resin can be transferred from the printer tank to the bottle
|
Always wear protective equipment when handling the resin:gogglesand nitrile gloves. |
Final processing of the finished 3D printout
- Ready model should be rinsed in isopropyl alcohol (IPA) or bioethanol for about 5 minutes.
- The manufacturer recommends the use of ultrasonic cleaner.
- Before further curing check if the model is completely dry after rinsing
- Place the rinsed parts in a well-ventilated room for at least 30 min. (Compressed air can also be used for at least 2 minutes).
- Cure the objects in a special chamber for 20 to 30 minutes at 65°C
- Recommended curing wavelength is from 300 nm to 410 nm
- During the grinding of resin it is absolutely necessary to remember about protection of airways
The packaging of Platinum SLA Series resins protects them from drying.
|
Please note that the printing method may vary depending on the printer used, its movement geometry, settings and the method of curing the model. |
Specification of Platinum SLA Series resin
- Viscosity: 700 cps at 25°C
- Density: 1.12 g/cm2
The table contains mechanical parameters of cured resin. Tested objects were cured for 30 minutes using high power LEDs.
| Parameter | Value | Test method |
|---|---|---|
| Glass transition temperature (Tg) | 54°C | ASTM D7028 |
| Water absorption | 0,3% | ASTM D570-98 |
| Impact strength (IZOD) | 15 J/m | ASTM D256A |
| Tensile Strength | 62 MPa | ASTM D638M |
| Tensile Resilience | 2200 MPa | ASTM D638M |
| Elongation at tension | 4% | ASTM D638M |
| Bending Strength | 75 MPa | ASTM D790M |
| Elasticity | 1900 MPa | ASTM D2240 |
| Shore Hardness | 78 | ASTM D2240 |