Description: 3D printer resin - PrimaCreator Value Water Washable UV Resin 500 ml - Black.
Resin inblack, used in 3D printers. The UV wavelength of the resin curing resin is in the rangefrom 395 nm to 405 nm. The product may emit an unpleasant smell of low intensity during operation. Resin residues from the model are removed with ordinary water. Finished prints can be dried in a specially designed chamber, or exposed to sunlight. They show a slight shrinkage. After final processing they are very hard. The product is sold in a bottle containing500 ml of resin.
PrimaCreator resins.
Printed from PrimaCreator resin.
Performance features of PrimaCreator resin
- Environmentally friendly printing:the resindoes not require the use of harmful rinsing chemicals for finished models
- The highest quality components were used to produce the resin
- Finished prints are characterized by a uniform colour with a semi-matt surface. They render details in detail, have smooth transitions between layers
- Designed mainly for lower power DLP printers using UV light to cure resin, includingZortrax InkspireandAnycubic Photon.
- May give off an unpleasant smell of low intensity
- Curing time of the resin is 4 to 8 seconds per coat
- Finished models can be dried in a special chamber from 2 to 5 minutes. In case of final curing in the sun, the printout should be exposed to UV radiation for 10 to 20 minutes. In case of limited sunlight, this time increases up to 60 minutes.
|
Always use protective measures when working with the resin: nitrileglassesand gloves. |
| Technical specifications | |
|---|---|
| Modulus of elasticity: | from 1,882 to 2,385 MPa |
| Bending strength: | from 40 to 58 MPa |
| Deformation temperature: | 80℃ |
| Thermal expansion: | 95 E-6 |
| Shrinkage value: | from 3.35% to 4.24% |
| Linear contraction: | 1.05% to 1.35% |
| Tensile strength: | from 30 to 52 MPa |
| Stretch module: | from 1,779 to 2,385 MPa |
| Extension at break: | from 4% to 10% |
| Shore hardness: | 85 to 88 D |
| Density: | from 1.05 to 1.25 g/cm3 |
| Impact: | 41 to 48 j/m |
| The viscosity: | from 100 to 350 MPa x s |
| UV wavelength of curing resin: | from 395 to 405 nm |