Product description: Filament Rosa3D BioWOOD 1.75 mm 0.5 kg - Beige
BioWOOD filament is a wood -like material, designed for 3D printers working in FFF / FDM technology. It is characterized by biodegradability, ease of printing, and the possibility of contact with food. The filament diameter is 1.75 mm . The material is made of a biopolymer consisting of 100% natural, renewable raw materials. Models made with the use of this material can be subjected to mechanical processing (grinding, turning, drilling, etc.) as well as painting and varnishing. BioWOOD gives off a delicate fragrance similar to natural wood.
In our offer of filaments you will also find other materials and colors.
Filament Rosa3D BioWOOD 1.75 mm 0.5 kg - Beige.
Main features of Wood material
- Made of natural biodegradable raw materials
- Recommended nozzle size is 0.5mm
- It simulates wood when printed
- It gives off a delicate scent similar to that of wood
- Possibility to sand and varnish the printed model
As the product is made of natural raw materials, each spool of BioWOOD may be slightly different in color, just like in nature.
Suggested filament printing parameters
| Printing temperature | 170 ° C to 210 ° C |
| Table temperature | 30 ° C to 50 ° C |
| Cooling the print | Recommended |
| Due to the differences in the design of printers, the above data should be treated as guidelines, and the appropriate values should be determined experimentally. |
Sample printout from BioWOOD filament.
Technical specification and physical properties of the filament
| Parameter | Range |
|---|---|
| Filament diameter | 1.75 mm |
| Filament dimensional tolerance | +/- 0.05 mm |
| Colour | Wood (beige) |
| Printing temperature | 170 ° C to 210 ° C |
| Recommended print speed | From 30 to 50 mm / s |
| Spool - material | BioWOOD |
| Spool diameter | 200 mm |
| Spool width | 55 mm |
| Mounting hole diameter | 52 mm |
| Desiccant | Yes |
| Vacuum packing | Yes |
| Material density | 1.26 g / cm 3 |
| Thermal deformation temperature | 55 ° C |
| Tensile strength at break | 34 MPa |
| Tensile modulus | 3200 MPa |
| Charpy Impact | 15 kJ / m 2 |
| Elongation when stretching | 3% |
| Print speed | From 60 to 80 mm / s |
| Net weight | 0.5 kg |