Product description: Filament Noctuo ABS - MMA 1.75 mm 0.25 kg - White
ABS-MMA is an innovative filament intended for 3D printing, which is an improved version of traditional ABS . It is characterized by an easier printing process and greater stiffness, which makes it an ideal choice for both beginners and intermediate users. When creating 3D prints, you can use an open printer without any problems, due to the lower emission of the characteristic styrene smell. Additionally, ABS-MMA exhibits high transparency , making it an attractive choice for creating transparent or translucent models. The filament also provides good mechanical strength and impact resistance, making it suitable for a variety of applications. The filament with a diameter of 1.75 mm, white , will work in most popular 3D printers for amateur home use and more.
Our filament offer also includes other materials and colors.
Filament properties
- Very easy to print
- Slight shrinkage
- Reduced styrene emissions
- High transparency
- Good mechanical strength, stiffness and hardness
- High impact resistance
- Good thermal stability
- Permissible continuous operation temperature above 75°C
- Average chemical resistance, in particular satisfactory resistance to alkalis, dilute acids, aliphatic hydrocarbons, oils and fats
- Good electrical insulating properties
Suggested filament printing parameters
| Head temperature | From 235°C to 260°C |
| Table temperature | From 90°C |
| Print cooling | Recommended |
|
Due to differences in the design of printers, the above data should be treated as guidelines and the appropriate values should be determined experimentally. |
Noctuo ABS - MMA filament 1.75 mm 0.25 kg - White.
Technical specifications and physical properties of the Noctuo ABS-MMA filament
| Parameter | Range |
|---|---|
| Color | White |
| Material | ABS-MMA |
| Filament diameter | 1.75mm |
| Density | 1.04 g/ cm3 |
| Water absorption until saturation | 3% |
| Print speed | < 200 mm/s |
| Vicat softening point | 96°C |
| Deflection temperature under load | 71°C |
| Notched impact strength according to Charpy | 22 kJ/ m2 |
| Elongation at break | 50% |
| Bending stress | 58 MPa |
| Flexural modulus in bending | 1750 MPa |
| Yield strength | 41 MPa |
| Product weight | 250 g net |