Product description: 3D printer resin - PrimaCreator Value Flex UV Resin 500 ml - Black.
PrimaCreator resin from the Flex line inblack, designed for 3D printers. Cured by UV light with wavelengthsfrom 395 nm to 405 nm. Models obtained after printing are flexible, show very small shrinkage. The cured resin has a high impact strength of 65 to 75 D Shore hardness scale. Finished models should be cleaned from resin residues with isopropyl alcohol (IPA). The product is sold in a500 mlbottle.
PrimaCreator Value Flex UV resin.
Printed from PrimaCreator resin.
Performance features of PrimaCreator resin
- Finished prints are characterized by a uniform colour with a semi-matt surface. They render details in detail, have smooth transitions between layers
- Highest quality components used for resin production
- Useisopropyl alcohol(IPA) to remove resin residues from the printed model.
- Designed mainly for DLP printers with a lower power UV light source used to cure resin, includingZortrax InkspireandAnycubic Photon.
- Prints prepared from resin, in addition to a high level of detail, show high hardness - on a Shore scale from 65 to 75 D
- The curing time depends on the colour of the resin and ranges from 4 to 12 seconds per coat.
- Finished models can be dried in a special UV chamber from 2 to 5 minutes. In the case of final curing in the sun, the printout should be exposed to UV for 10 to 20 minutes. In case of limited sunlight, this time increases up to 60 minutes.
|
Always use protective measures when working with the resin: nitrileglassesand gloves. |
| Technical specifications | |
|---|---|
| Modulus of elasticity: | from 1,882 to 2,385 MPa |
| Bending strength: | 40 to 70 MPa |
| Deformation temperature: | 80°C |
| Thermal expansion: | 95 E-6 |
| Shrinkage value: | from 3.72% to 4.24% |
| Linear contraction: | from 1.05% to 1.35% |
| Tensile strength: | from 30 to 52 MPa |
| Stretch module: | from 1,779 to 2,385 MPa |
| Extension at break: | 130% |
| Shore hardness: | 65 to 75 D |
| The glass transition temperature: | 100°C |
| Density: | from 1.05 to 1.25 g/cm3 |
| Impact: | 41 to 48 j/m |
| The viscosity: | from 1050 to 300 MPa x s |
| Curing time: | 4 to 12 s for 0.005 mm layer |
| UV wavelength of curing resin: | from 395 to 405 nm |